PT. TUNAS TASIKA solvent free, single component epoxy coating, which cures in contact with hot surfaces and is designed to prevent or protect metal from corrosion under insulation (CUI). Belzona 5851 (HA-Barrier) can be easily applied by brush and does not require any weighing or mixing.
This heat activated material can be applied directly onto hot surfaces (70-150°C / 158-302°F) with minimal surface preparation, avoiding production downtime. Once cured, it provides outstanding corrosion protection. Also available is Belzona 1251 (HA-Barrier), a heat-activated epoxy repair composite which can be used in fill pitting and bond equipment among other applications.
Key benefits:
- In-situ application to live equipment operating at high temperature with minimal surface preparation
- Single pack system, no weighing or mixing required
- Reduced health and safety risks as it is solvent free and no hot work is required
- Fast cure allowing equipment to be re-insulated with minimum delay
- Excellent corrosion protection
- Good chemical resistance against a wide range of chemicals
- Excellent adhesion to (even to manually prepared) metals including stainless steel, carbon steel, aluminium, brass and copper
- Thermally stable up to 150°C (302°F) in dry conditions
Applications for Belzona 5851 (HA-Barrier) include:
- Prevention of corrosion under insulation (CUI)
- Long-term corrosion protection of hot pipework and process equipment
- In-situ external coating of process vessels during service operating at high temperature avoiding production downtime
| Key technical data: | |
|---|---|
| Working life | Unlimited *cure will not commence until the product is heated |
| Time to full cure 100°C (212°F) | 2 days |
| Coverage rate (1kg) | 2.4 m2 (25 sq.ft.) at 200 microns (8 mils) per coat |
| Volume capacity (1kg) | 476 cm3 (29 cu.in.) |
| Heat resistance | Up to 150°C (302°F) |
| Heat distortion temperature (tested per ASTM D648) | 127°C (261°F) after 7 days cure at 100°C (212°F) |
| Bonds to | Aluminium, copper, steel, stainless steel, cast iron, and other metals |
| Typical applications | Protection against CUI problems, heat activated coating for live process equipment |