PT. TUNAS TASIKA 2-part repair composite for metal repair and resurfacing based on solvent free epoxy resin reinforced with silicon steel alloy. This repair material will not corrode and resists a wide range of chemicals. It is easy to mix and apply without the need of specialist tools and can be machined using conventional tools.
Key benefits:
- Multi-purpose durable repair composite
- Fully machinable using conventional tools
- Application and cure at room temperature – no hot work involved
- Simple mixing ratio
- Reduced health and safety risks as it is solvent free
- No shrinkage, expansion or distortion
- Excellent adhesion to metals including stainless steel, carbon steel, aluminium, brass and copper
- Will adhere to many other natural and synthetic materials including glass and wood
- Outstanding corrosion resistance
- Excellent chemical resistance against a wide range of chemicals
- Excellent electrical insulation characteristics
Applications for Belzona 1111 (Super Metal) include:
- Repair of cracks and holes on engine and pump casings, pipes, tanks and other equipment
- Resurface of pitted metal surfaces
- Repair of damaged shafts and hydraulic rams
- In situ flange repair
- High strength structural adhesive for metal bonding
- Creation of irregular load bearing shims and reforming of bearing housings
| Key technical data: | |
|---|---|
| Working life at 25°C (77°F) | 15 minutes |
| Time to immersion service at 25°C (77°F) | 20 hours |
| Pull off adhesion (D4541 / ISO 4624) | 3,240 psi (22.33MPa) ambient cure on blasted mild steel |
| Compressive strength (ASTM D695) | 12,900 psi (88.9MPa) ambient cure |
| Temperature resistance | 93°C (200°F) immersed, 200°C (392°F) dry |
| Bonds to | Aluminium, copper, steel, stainless steel, cast iron, lead, glass, wood and many more |
| Typical applications | Bonding, shimming, filling, gluing, patch repairs and many more |